Four Mobi-Mat ®Types
Colors
Finishing options
Product Range
| MOBI-MAT ® TYPE |
LX
|
A2X
|
MM3V25
|
MM2C25
|
| Weight * |
0,14 psf
(0,7 kg/m²) |
0,34 psf
(1,65 kg/m²) |
1,64 psf
(8 kg/m²) |
1,23 psf
(6 kg/m²) |
| Composition |
100% Polyester
|
|||
* The weight can vary according to the finishing of the matting.
Mechanical properties
Test method : Lab-TME 2T : adapted from NF G 071-119 or NEQ 5081
| MOBI-MAT ® TYPE |
LX
|
A2X
|
MM3V25
|
MM2C25
|
| Tensile strength (wrap direction) / 4m20 |
Min. 24 tons
|
Min. 46 tons
|
Min. 105 tons
|
|
| Tensile strength (warp direction) |
Min. 56 kN/m
or 5,7 t/m |
Min. 135 kN/m
or 13,8 t/m |
Min. 245 kN/m
or 25 t/m |
|
| Elongation at break (%) |
21%
|
30%
|
||
| compression |
12 Mpa (N/mm²)
|
|||
Chemical properties
| MOBI-MAT ® TYPE |
LX
|
A2X
|
MM3V25
|
MM2C25
|
| Moisture regain 20°C - 65% HR |
12 Mpa (N/mm²)
|
|||
| Acid resistance |
Good
|
|||
| Alkali resistance |
Good
|
|||
| Solvent resistance |
Good
|
|||
| POL resistance |
Good
|
|||
| Aviation Synthetic Hydraulic Fluid Resistance |
Excellent at ambient temperature
(no physical deterioration after 18 days of wetting, 100% mechanical characteristices) |
|||
| UV and weather resistance |
Good
|
|||
| Micro-organisms resistance |
Excellent
|
|||
| Urea and Liquid manure resistance |
Excellent : placed for 6 months under a cow manager,
MOBI-MAT ® showed no physical degradation |
|||
Thermal properties
| MOBI-MAT ® TYPE |
LX
|
A2X
|
MM3V25
|
MM2C25
|
| Useable temperature |
-40°F (-40°C) / 176°F (+ 80°C)
|
|||
| Softening temperature |
428°F (220°C)
|
|||
| Melting temperature |
500°F (260°C)
|
|||
| Degradation temperature |
572°F (300°C)
|
|||
| Combustion temperature |
Laid on the ground, the mat stops burning
slowly as soon as the flame is taken away |
|||
Composite bars properties
| MOBI-MAT ® TYPE |
LX
|
A2X
|
MM3V25
|
MM2C25
|
| Composition |
-
|
Fiberglass
|
Carbon fibers
|
|
| Color |
-
|
White
|
Black
|
|
| Electrical property |
-
|
Non conduction
|
Conductible
|
|
| Combustion |
-
|
Fiberglass incombustible
|
Stops burning when the flame is taken away
|
|
| Flexural modulus |
-
|
47.6 GPa
|
109.9 GPa
|
|
| Flexural strength |
-
|
1000 MPa
|
1627 MPa
|
|
| Crush test method 12 CER2-TR1 |
-
|
24.1 MPa
|
25.9 MPa
|
|